Product Introduction
UNS N06035 is a nickel-based alloy with a high chromium content that offers superior corrosion resistance to commercial phosphoric acid and to the mixed environments of many highly [TJC STAINLESS]oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid than most other nickel - and iron-based alloys. The N06035 alloy prevents the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications.
Chemical composition (%):
N06035 Alloy
Ni:Rest; Cr: 32.25-34.25; Mo: 7.6-9; Fe:≤2; Co:≤1; W: 0.6 or less. Mn: 0.5 or less; Si: 0.6 or less; C: 0.05 or less; [TJC STAINLESS]Al: 0.4 or less; P: 0.03 or less. S: 0.015 or less; Cu: 0.30 or less; V: 0.2 or less.
Physical Property
Density: 8.9 g/cm after;
Melting Point:1331-1361℃;[TJC STAINLESS]
Mechanical properties /MPa(Room Temperature):
Heat Treatment: Annealed;
Tensile Strength:≥586;
Yield Strength:≥241;
Elongation/A5%:≥30%;
Product standard
ASTM B574,ASTM B575, [TJC STAINLESS]ASTM B564, ASTM B619, ASTM B622, ASTM B626, ASTM B366, ASTM B462, ASTM B472.
Application field
● Evaporator for wet phosphoric acid production
● Pickling equipment using nitric acid and hydrofluoric acid
● caustic soda[TJC STAINLESS] neutralization system
● Chemical systems involving nitric acid and chloride
UNS N06035 is a nickel-based alloy with a high chromium content that offers superior corrosion resistance to commercial phosphoric acid and to the mixed environments of many highly [TJC STAINLESS]oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid than most other nickel - and iron-based alloys. The N06035 alloy prevents the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications.
Chemical composition (%):
N06035 Alloy
Ni:Rest; Cr: 32.25-34.25; Mo: 7.6-9; Fe:≤2; Co:≤1; W: 0.6 or less. Mn: 0.5 or less; Si: 0.6 or less; C: 0.05 or less; [TJC STAINLESS]Al: 0.4 or less; P: 0.03 or less. S: 0.015 or less; Cu: 0.30 or less; V: 0.2 or less.
Physical Property
Density: 8.9 g/cm after;
Melting Point:1331-1361℃;[TJC STAINLESS]
Mechanical properties /MPa(Room Temperature):
Heat Treatment: Annealed;
Tensile Strength:≥586;
Yield Strength:≥241;
Elongation/A5%:≥30%;
Product standard
ASTM B574,ASTM B575, [TJC STAINLESS]ASTM B564, ASTM B619, ASTM B622, ASTM B626, ASTM B366, ASTM B462, ASTM B472.
Application field
● Evaporator for wet phosphoric acid production
● Pickling equipment using nitric acid and hydrofluoric acid
● caustic soda[TJC STAINLESS] neutralization system
● Chemical systems involving nitric acid and chloride