STAINLESS STEEL CLAD PLATE
Stainless Steel Clad Plate is joint by carbon steel(base material) and stainless steel(clad material),which forms a kind of alloy-integrate of carbon steel and stainless steel.
The base material for clad plate could be common carbon steel such as Q235B,A516Gr70,20R,Q345R,16MnR,etc
while 304,304L,316,316L,1Cr13 and duplex stainless could be taken for clad material.The type of materials can be chosen freely according diffrent requirement from customers.As a kind of resource-saving product with reducing consumption of noble metal and construction cost for project,which realizes perfect match for low-cost and high property in use.
Application:
Stainless steel clad plate is widely used in petroleum,chemical,salt industry,food industry,water and electric conservancy,dish head for boiler,pressure,etc.
Advantage for Stainless Steel Clad Plate:
Stainless steel clad plate is not only with stainless' good anti-corrosion nature,also performs well in mechanical and machining properties,which could be taken hot-press,cold-bend,cutting welding process.So this material is treated a new kind of industrial products.
Machining Methods for Stainless Steel Clad Plate:
Explosive Clad:Overlap stainless plate on carbon steel plate with a cushion in middle to leave certain space.Explosive material will be paved on the surface of stainless plate and when explosive material exploding,high energy can make stainless plate impact carbon steel plate with high speed to joint.In ideal condition,the strength for square mm could reach 400 Mpa.
Thickness Scope:10mm-300mm
Hot Rolled Clad:Hot rolled stainless steel clad plate is rolled of stainless and carbon steel plates in vacuum condition.In such process,the clad plate and base plate should be in pure clean condition.Besides,for improving the strength of conbining,there are also a series of technical methods with physics and chemical treatments.
Thickness Scope:0.6mm-50mm
Cold Rolled Clad:Cold rolled Stainless clad plate is made after annealing-pickling-cold rold-mid annealing-pickling production process to stainless steel clad plates.This material is with better yield strength than same grade stainless plate.Min thickness would reach 0.6mm.
The base material for clad plate could be common carbon steel such as Q235B,A516Gr70,20R,Q345R,16MnR,etc
while 304,304L,316,316L,1Cr13 and duplex stainless could be taken for clad material.The type of materials can be chosen freely according diffrent requirement from customers.As a kind of resource-saving product with reducing consumption of noble metal and construction cost for project,which realizes perfect match for low-cost and high property in use.
Application:
Stainless steel clad plate is widely used in petroleum,chemical,salt industry,food industry,water and electric conservancy,dish head for boiler,pressure,etc.
Advantage for Stainless Steel Clad Plate:
Stainless steel clad plate is not only with stainless' good anti-corrosion nature,also performs well in mechanical and machining properties,which could be taken hot-press,cold-bend,cutting welding process.So this material is treated a new kind of industrial products.
Machining Methods for Stainless Steel Clad Plate:
Explosive Clad:Overlap stainless plate on carbon steel plate with a cushion in middle to leave certain space.Explosive material will be paved on the surface of stainless plate and when explosive material exploding,high energy can make stainless plate impact carbon steel plate with high speed to joint.In ideal condition,the strength for square mm could reach 400 Mpa.
Thickness Scope:10mm-300mm
Hot Rolled Clad:Hot rolled stainless steel clad plate is rolled of stainless and carbon steel plates in vacuum condition.In such process,the clad plate and base plate should be in pure clean condition.Besides,for improving the strength of conbining,there are also a series of technical methods with physics and chemical treatments.
Thickness Scope:0.6mm-50mm
Cold Rolled Clad:Cold rolled Stainless clad plate is made after annealing-pickling-cold rold-mid annealing-pickling production process to stainless steel clad plates.This material is with better yield strength than same grade stainless plate.Min thickness would reach 0.6mm.