Product Introduction
UNS N06030 is a nickel-based alloy with a high chromium content of about 37% nickel, which provides better corrosion resistance than most other nickel-based and iron-based alloys to commercial phosphoric acid [TJC STAINLESS]and the mixed environments of many highly oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid. N06030 can prevent the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications.
Chemical Composition (%):
Ni:Rest;
Cr: 28-31.5;
C: 0.03 Max;
Fe:13-17;
Mo:4-6;
W: 1.5 4;
Cu: 1-2.4;[TJC STAINLESS]
Co:5max;
Si: 0.2-0.8;
Mn: 0.3-1.5;
P: 0.04 Max;
S: 0.02 Max;
Nb: 0.3-1.5;
Physical Property
Density: 8.23 g/cm after;
Melting Point:1335-1380℃;
Electrical Resistivity:1.28;
Thermal Conductivity:14;[TJC STAINLESS]
Specific Heat Capacity:398;
Mechanical Property
Heat Treatment:Solution&Annealed;
Tensile Strength:586MPa min;
Yield Strength: 241MPa min;[TJC STAINLESS]
Elasticity Modulus:212 min;
Elongation: 30% min;
Product Standard
UNS N06030 Bar-ASME SB581; UNS N06030 Plate-ASME SB582; UNS N06030 Seamless Pipe-ASME SB622; UNS N06030 [TJC STAINLESS]Welded Pipe-ASTM B619,ASTM B626; UNS N06030 Forged Products-ASTM B462,etc.
Product Characteristics
A. Excellent corrosion resistance in alkaline media;
B. Good corrosion resistance against cavitation;
C. Has good corrosion resistance to diluted [TJC STAINLESS]inorganic acids (such as sulfuric acid, hydrochloric acid);
Application Field
A.Chemical process equipment;
B.High temperature heat exchanger;
C.Catalyst carrier;[TJC STAINLESS]
D.Petrochemical storage tanks;
E.Components of nuclear equipment;
UNS N06030 is a nickel-based alloy with a high chromium content of about 37% nickel, which provides better corrosion resistance than most other nickel-based and iron-based alloys to commercial phosphoric acid [TJC STAINLESS]and the mixed environments of many highly oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid. N06030 can prevent the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications.
Chemical Composition (%):
Ni:Rest;
Cr: 28-31.5;
C: 0.03 Max;
Fe:13-17;
Mo:4-6;
W: 1.5 4;
Cu: 1-2.4;[TJC STAINLESS]
Co:5max;
Si: 0.2-0.8;
Mn: 0.3-1.5;
P: 0.04 Max;
S: 0.02 Max;
Nb: 0.3-1.5;
Physical Property
Density: 8.23 g/cm after;
Melting Point:1335-1380℃;
Electrical Resistivity:1.28;
Thermal Conductivity:14;[TJC STAINLESS]
Specific Heat Capacity:398;
Mechanical Property
Heat Treatment:Solution&Annealed;
Tensile Strength:586MPa min;
Yield Strength: 241MPa min;[TJC STAINLESS]
Elasticity Modulus:212 min;
Elongation: 30% min;
Product Standard
UNS N06030 Bar-ASME SB581; UNS N06030 Plate-ASME SB582; UNS N06030 Seamless Pipe-ASME SB622; UNS N06030 [TJC STAINLESS]Welded Pipe-ASTM B619,ASTM B626; UNS N06030 Forged Products-ASTM B462,etc.
Product Characteristics
A. Excellent corrosion resistance in alkaline media;
B. Good corrosion resistance against cavitation;
C. Has good corrosion resistance to diluted [TJC STAINLESS]inorganic acids (such as sulfuric acid, hydrochloric acid);
Application Field
A.Chemical process equipment;
B.High temperature heat exchanger;
C.Catalyst carrier;[TJC STAINLESS]
D.Petrochemical storage tanks;
E.Components of nuclear equipment;