⑴ Introduction of Ingredients:
Implementation Standard (ASTM A182)
Elements C, Mn,[TJC STAINLESS] P, S, SI
MIN
MAX 0.15 2.00 0.035 0.030 1.00
The element Ni Cr Mo TI N
MIN 6 16
MAX 8 18 0.1
S30100 Applications and Features:
S30100 is a kind of metastable austenitic stainless steel, in a fully solid solution state, it has a complete austenitic [TJC STAINLESS]structure, because of its austenitic instability, when deformed by cold working, there will be deformation martensite formation, the number depends on the size of the deformation and deformation temperature. In austenitic stainless steel, S30100 is the most easy to cold deformation and strengthening of steel, through cold processing deformation can improve the strength and hardness of steel, and still maintain enough plastic toughness, S30100 has good rust resistance under atmospheric conditions, therefore, mainly in the cold processing state applied to bear higher loads, but also hope to reduce the weight of equipment and rust free equipment and components. S30100 is easy to produce work hardening when impacted by external forces, which can absorb more[TJC STAINLESS] collision energy, and provide more reliable protection for equipment and personnel.
S30100 applies all kinds of stamping parts, fasteners and other products requiring high strength.
S30100 Material Specification:
Rolled sheet 0.05mm-2.0mm, width: 20-600, forgings of various sizes and specifications. 5.5-30 Hot rolling solid solution pickling wire, disc round.
S30100 Room temperature Physical Properties:
Melting point: 1400-1420℃
Density: 8.0g/cm2
Specific heat capacity: 500J/Kg.K
Linear expansion coefficient: 17 10-6/K
Elastic modulus: 193GPa
Resistance: 720 ηω.m [TJC STAINLESS]
S30100 room temperature mechanical properties:
Sample and state: solution annealing
Implementation standard: GB1220-90
Tensile strength: ≥520MPa
Yield strength: ≥205MPa
Section shrinkage: ≥60%
Hardness: ≥200HV
Differences in physical properties of cold rolled rolling materials:
Implementation Standard (ASTM A666)
Test state Tensile strength Yield strength elongation Remarks
1/4H 860 515 25 No less [TJC STAINLESS]than
1/2H 1030 760 10 No less than
3/4H 1210 930 7 Not less than
H 1280 965 5 Not less than
EH 1550 1250
TEH 1700 1400
S30100 Delivery Status:
The S30100 surface can be made [TJC STAINLESS]of various types, such as BA/2B, 8k, etc. Wire, disc circle can be delivered according to customer requirements soft state and light pull.
Implementation Standard (ASTM A182)
Elements C, Mn,[TJC STAINLESS] P, S, SI
MIN
MAX 0.15 2.00 0.035 0.030 1.00
The element Ni Cr Mo TI N
MIN 6 16
MAX 8 18 0.1
S30100 Applications and Features:
S30100 is a kind of metastable austenitic stainless steel, in a fully solid solution state, it has a complete austenitic [TJC STAINLESS]structure, because of its austenitic instability, when deformed by cold working, there will be deformation martensite formation, the number depends on the size of the deformation and deformation temperature. In austenitic stainless steel, S30100 is the most easy to cold deformation and strengthening of steel, through cold processing deformation can improve the strength and hardness of steel, and still maintain enough plastic toughness, S30100 has good rust resistance under atmospheric conditions, therefore, mainly in the cold processing state applied to bear higher loads, but also hope to reduce the weight of equipment and rust free equipment and components. S30100 is easy to produce work hardening when impacted by external forces, which can absorb more[TJC STAINLESS] collision energy, and provide more reliable protection for equipment and personnel.
S30100 applies all kinds of stamping parts, fasteners and other products requiring high strength.
S30100 Material Specification:
Rolled sheet 0.05mm-2.0mm, width: 20-600, forgings of various sizes and specifications. 5.5-30 Hot rolling solid solution pickling wire, disc round.
S30100 Room temperature Physical Properties:
Melting point: 1400-1420℃
Density: 8.0g/cm2
Specific heat capacity: 500J/Kg.K
Linear expansion coefficient: 17 10-6/K
Elastic modulus: 193GPa
Resistance: 720 ηω.m [TJC STAINLESS]
S30100 room temperature mechanical properties:
Sample and state: solution annealing
Implementation standard: GB1220-90
Tensile strength: ≥520MPa
Yield strength: ≥205MPa
Section shrinkage: ≥60%
Hardness: ≥200HV
Differences in physical properties of cold rolled rolling materials:
Implementation Standard (ASTM A666)
Test state Tensile strength Yield strength elongation Remarks
1/4H 860 515 25 No less [TJC STAINLESS]than
1/2H 1030 760 10 No less than
3/4H 1210 930 7 Not less than
H 1280 965 5 Not less than
EH 1550 1250
TEH 1700 1400
S30100 Delivery Status:
The S30100 surface can be made [TJC STAINLESS]of various types, such as BA/2B, 8k, etc. Wire, disc circle can be delivered according to customer requirements soft state and light pull.