Inconel 601 alloy, an alloy material.Have excellent oxidation resistance at high temperature, good carbonization resistance, good resistance to oxidation sulfur atmosphere, at room temperature and has good mechanical properties at high temperature as good resistance to stress corrosion cracking performance due to control the carbon content and grain size, 601[TJC STEEL] had a higher creep rupture strength, therefore it is recommended to use in the field of above 500 ℃, 601.
The Characteristics of Inconel 601 Alloy:
1. Excellent oxidation resistance at high temperature
2. Good carbonization resistance
3. It has good antioxidant and sulfur atmosphere
4. Good mechanical properties at room temperature and high temperature
5. Good resistance to stress corrosion cracking due[TJC STEEL] to the control of carbon content and grain size, 601 has a high creep fracture strength, so 601 is recommended to be used in the field above 500℃.
Metallographic structure of Inconel 601 Alloy:
601 is surface centered cubic lattice structure.
Corrosion Resistance of Inconel 601 Alloy:
An important property of 601 alloy is its [TJC STEEL]ability to resist oxidation at temperatures up to 1180℃.Even under very harsh conditions, such as during heating and cooling cycles, 601 can produce a dense oxide film for high spalling resistance.601 has good resistance to carbonation.Due to the high content of chromium and aluminum, 601 has a good oxidation resistance in high temperature [TJC STEEL]sulfur-containing atmosphere.
Application of Inconel 601 Alloy
1. Pallets, baskets and fixtures for heat treatment plant.
2. Steel wire split annealing and radiation tube, high speed gas burner, industrial furnace in the mesh belt.
3. Isolation tank in ammonia reforming [TJC STEEL]and catalytic support grid in nitric acid manufacturing.
4. Exhaust system components
5. Combustion chamber of solid waste incinerator
6.Pipe support and soot handling components
7.Exhaust gas detoxification system components
8.Oxygen reheater equipments
Chemical Composition for Inconel 601 Alloy
GRADE % Ni Cr Fe C Mn Si Cu Al P S
601 MIN 58 21 1
MAX 63 25 Rest 0.1 1.5 0.5 1 1.7 0.02 0.015
Physical Property for Inconel 601 Alloy
Density 8.1 g/cm3
Melting Point 1320-1370℃
Mechanical Property for Inconel 601 Alloy
Heat Treatment Tensile Strength Rm N/mm2 Yield Strength RP0.2N/mm2 Elongation A5 % Brinell Hardness
HB
Annealling 650 300 30 -
Solid Solution 600 240 30 ≤220
[email protected]
The Characteristics of Inconel 601 Alloy:
1. Excellent oxidation resistance at high temperature
2. Good carbonization resistance
3. It has good antioxidant and sulfur atmosphere
4. Good mechanical properties at room temperature and high temperature
5. Good resistance to stress corrosion cracking due[TJC STEEL] to the control of carbon content and grain size, 601 has a high creep fracture strength, so 601 is recommended to be used in the field above 500℃.
Metallographic structure of Inconel 601 Alloy:
601 is surface centered cubic lattice structure.
Corrosion Resistance of Inconel 601 Alloy:
An important property of 601 alloy is its [TJC STEEL]ability to resist oxidation at temperatures up to 1180℃.Even under very harsh conditions, such as during heating and cooling cycles, 601 can produce a dense oxide film for high spalling resistance.601 has good resistance to carbonation.Due to the high content of chromium and aluminum, 601 has a good oxidation resistance in high temperature [TJC STEEL]sulfur-containing atmosphere.
Application of Inconel 601 Alloy
1. Pallets, baskets and fixtures for heat treatment plant.
2. Steel wire split annealing and radiation tube, high speed gas burner, industrial furnace in the mesh belt.
3. Isolation tank in ammonia reforming [TJC STEEL]and catalytic support grid in nitric acid manufacturing.
4. Exhaust system components
5. Combustion chamber of solid waste incinerator
6.Pipe support and soot handling components
7.Exhaust gas detoxification system components
8.Oxygen reheater equipments
Chemical Composition for Inconel 601 Alloy
GRADE % Ni Cr Fe C Mn Si Cu Al P S
601 MIN 58 21 1
MAX 63 25 Rest 0.1 1.5 0.5 1 1.7 0.02 0.015
Physical Property for Inconel 601 Alloy
Density 8.1 g/cm3
Melting Point 1320-1370℃
Mechanical Property for Inconel 601 Alloy
Heat Treatment Tensile Strength Rm N/mm2 Yield Strength RP0.2N/mm2 Elongation A5 % Brinell Hardness
HB
Annealling 650 300 30 -
Solid Solution 600 240 30 ≤220
[email protected]