GH3536 is a nickel-based superalloy with high iron content, mainly reinforced by solid solution of chromium and molybdenum, with a density [TJC STAINLESS]of 8.3g/cm3.The most well-known commercial grade of the same steel is Hastelloy ® X Alloy.
National Standard
CHINA GB/T 14992-2005 GH3536(GH536)
AMERICA ASTM B572-2011 UNS N06002
HAYNES HASTELLOY® X alloy
JAPAN JIS H 4551-2000 NW6002
NiCr21Fe18Mo9
NIPPON YAKIN NAS HX
GERMANY DIN 17744-2002 2.4665
NiCr22Fe18Mo
VDM Metals[TJC STAINLESS] Nicrofer®4722 Co
alloy X
Component Specification
GRADE GH3536 N06002 NW6002 2.4665
C 0.05~0.15 0.05~0.15 0.05~0.15 0.05~0.15
Si ≤1.00 ≤1.00 ≤1.00 ≤1.00
Mn ≤1.00 ≤1.00 ≤1.00 ≤1.00
P ≤0.025 ≤0.040 ≤0.040 ≤0.020
S ≤0.015 ≤0.030 ≤0.030 ≤0.015
Ni -- Remainder[TJC STAINLESS] -- Other
Cr 20.5~23.0 20.5~23.0 20.5~23.0 20.5~23.0
Mo 8.0~10.0 8.0~10.0 8.0~10.0 8.0~10.0
Fe 17.0~20.0 17.0~20.0 17.0~20.0 17.0~20.0
Co 0.5~2.5 0.5~2.5 0.5~2.5 0.5~2.5
W 0.2~1.0 0.2~1.0 0.2~1.0 0.2~1.0
Al ≤0.50 -- -- ≤0.50
Ti ≤0.15 -- -- --
Cu ≤0.50 -- -- ≤0.50
B ≤0.01 -- ≤0.01 ≤0.01
Application:
GH3536 alloy under the high temperature of 1200 ℃, still has a very high strength and oxidation resistance, combined with excellent forming and welding performance, and excellent resistance to stress corrosion cracking performance, is widely used in gas turbine, industrial furnace, heat treatment equipment and the process of [TJC STAINLESS]nuclear components, such as gas turbine combustion cylinder, burner taper pipe, transition, spray rod, distillation and the chemical industry, muffle furnace, catalyst support grille, hearth baffle, pyrolysis operation and flash drier parts of pipes, etc.
National Standard
CHINA GB/T 14992-2005 GH3536(GH536)
AMERICA ASTM B572-2011 UNS N06002
HAYNES HASTELLOY® X alloy
JAPAN JIS H 4551-2000 NW6002
NiCr21Fe18Mo9
NIPPON YAKIN NAS HX
GERMANY DIN 17744-2002 2.4665
NiCr22Fe18Mo
VDM Metals[TJC STAINLESS] Nicrofer®4722 Co
alloy X
Component Specification
GRADE GH3536 N06002 NW6002 2.4665
C 0.05~0.15 0.05~0.15 0.05~0.15 0.05~0.15
Si ≤1.00 ≤1.00 ≤1.00 ≤1.00
Mn ≤1.00 ≤1.00 ≤1.00 ≤1.00
P ≤0.025 ≤0.040 ≤0.040 ≤0.020
S ≤0.015 ≤0.030 ≤0.030 ≤0.015
Ni -- Remainder[TJC STAINLESS] -- Other
Cr 20.5~23.0 20.5~23.0 20.5~23.0 20.5~23.0
Mo 8.0~10.0 8.0~10.0 8.0~10.0 8.0~10.0
Fe 17.0~20.0 17.0~20.0 17.0~20.0 17.0~20.0
Co 0.5~2.5 0.5~2.5 0.5~2.5 0.5~2.5
W 0.2~1.0 0.2~1.0 0.2~1.0 0.2~1.0
Al ≤0.50 -- -- ≤0.50
Ti ≤0.15 -- -- --
Cu ≤0.50 -- -- ≤0.50
B ≤0.01 -- ≤0.01 ≤0.01
Application:
GH3536 alloy under the high temperature of 1200 ℃, still has a very high strength and oxidation resistance, combined with excellent forming and welding performance, and excellent resistance to stress corrosion cracking performance, is widely used in gas turbine, industrial furnace, heat treatment equipment and the process of [TJC STAINLESS]nuclear components, such as gas turbine combustion cylinder, burner taper pipe, transition, spray rod, distillation and the chemical industry, muffle furnace, catalyst support grille, hearth baffle, pyrolysis operation and flash drier parts of pipes, etc.