Hastelloy C-22 alloy is a general Ni-Cr-Mo alloy with a density of 8.7g/cm3.Compared with the common Ni-Cr-Mo alloy, such as C-276, C-4, [TJC STAINLESS]625 alloy, it has better and more comprehensive corrosion resistance.
National Standard
CHINA GB/T 15007-2008 NS3308
AMERICA ASTM B462-2006
ASTM B574-2006
ASTM B575-2006 N06022
Special Metals INCONEL® alloy 22
Haynes International HASTELLOY® C-22®
JAPAN JIS H 4551:2000 NW6022
Nippon Yakin[TJC STAINLESS] NAS NW22
GERMANY DIN 17744:2002 NiCr21Mo14W
2.4602
VDM Metals VDM® Alloy 22
Nicrofer® 5621 hMoW
Component Specification
GRADE NS3308 N06022 NW6022 2.4602
C ≤0.015 ≤0.015 ≤0.015 ≤0.010
Si ≤0.08 ≤0.08[TJC STAINLESS] ≤0.08 ≤0.08
Mn ≤0.50 ≤0.50 ≤0.50 ≤0.50
P ≤0.020 ≤0.020 ≤0.025 ≤0.025
S ≤0.020 ≤0.020 ≤0.020 ≤0.015
Ni --- Remainder --- Other
Cr 20.0~22.5 20.0~22.5 20.0~22.5 20.0~22.5
Mo 12.5~14.5 12.5~14.5 12.5~14.5 12.5~14.5
Fe 2.0~6.0 2.0~6.0 2.0~6.0 2.0~6.0
W 2.5~3.5 2.5~3.5 2.5~3.5 2.5~3.5
Co ≤2.50 ≤2.50 ≤2.50 ≤2.50
V ≤0.35 ≤0.35 ≤0.35 ≤0.35
Material Characteristics:
(1) Excellent resistance to various corrosive media under oxidation and reduction conditions;It is one of the few materials that can resist the corrosion of moist chlorine gas, hypochlorite and chlorine dioxide solution, and has[TJC STAINLESS] significant corrosion resistance to high concentration of salt chloride solution (such as ferric chloride and copper chloride).
(2) It can also resist a variety of corrosive [TJC STAINLESS]environments at a high temperature of up to 677℃.
(3)Good resistance to pitting corrosion, crevice corrosion and stress corrosion cracking.
(4) Excellent welding performance.
Applications:
Hastelloy C-22 alloy has been widely used in chemical and petrochemical fields, such as the application in the contact with chloride-containing organic components and catalytic systems.This material is especially suitable for high temperature, mixed with impurities of inorganic acids and organic acids (such as formic acid and acetic acid), sea water corrosion environment.
National Standard
CHINA GB/T 15007-2008 NS3308
AMERICA ASTM B462-2006
ASTM B574-2006
ASTM B575-2006 N06022
Special Metals INCONEL® alloy 22
Haynes International HASTELLOY® C-22®
JAPAN JIS H 4551:2000 NW6022
Nippon Yakin[TJC STAINLESS] NAS NW22
GERMANY DIN 17744:2002 NiCr21Mo14W
2.4602
VDM Metals VDM® Alloy 22
Nicrofer® 5621 hMoW
Component Specification
GRADE NS3308 N06022 NW6022 2.4602
C ≤0.015 ≤0.015 ≤0.015 ≤0.010
Si ≤0.08 ≤0.08[TJC STAINLESS] ≤0.08 ≤0.08
Mn ≤0.50 ≤0.50 ≤0.50 ≤0.50
P ≤0.020 ≤0.020 ≤0.025 ≤0.025
S ≤0.020 ≤0.020 ≤0.020 ≤0.015
Ni --- Remainder --- Other
Cr 20.0~22.5 20.0~22.5 20.0~22.5 20.0~22.5
Mo 12.5~14.5 12.5~14.5 12.5~14.5 12.5~14.5
Fe 2.0~6.0 2.0~6.0 2.0~6.0 2.0~6.0
W 2.5~3.5 2.5~3.5 2.5~3.5 2.5~3.5
Co ≤2.50 ≤2.50 ≤2.50 ≤2.50
V ≤0.35 ≤0.35 ≤0.35 ≤0.35
Material Characteristics:
(1) Excellent resistance to various corrosive media under oxidation and reduction conditions;It is one of the few materials that can resist the corrosion of moist chlorine gas, hypochlorite and chlorine dioxide solution, and has[TJC STAINLESS] significant corrosion resistance to high concentration of salt chloride solution (such as ferric chloride and copper chloride).
(2) It can also resist a variety of corrosive [TJC STAINLESS]environments at a high temperature of up to 677℃.
(3)Good resistance to pitting corrosion, crevice corrosion and stress corrosion cracking.
(4) Excellent welding performance.
Applications:
Hastelloy C-22 alloy has been widely used in chemical and petrochemical fields, such as the application in the contact with chloride-containing organic components and catalytic systems.This material is especially suitable for high temperature, mixed with impurities of inorganic acids and organic acids (such as formic acid and acetic acid), sea water corrosion environment.