F62, Incoloy25-6HN Contains Six Mo Super Austenitic Stainless Steels:
AL-6XN (N08367) super austenitic stainless steel is a kind of excellent resistance to pitting and crevice corrosion of chlorine ion capacity of super austenitic stainless steel, as a kind of good cost performance of corrosion-resistant alloy, its comprehensive corrosion resistant ability than 316 l had the very big spanning, at the same time [TJC STAINLESS]relative to the C - 276 and other corrosion resistance of nickel base alloy close to its corrosion resistance ability, cost advantage is obvious.Because the visible part of nitrogen is added in the alloy, so that the AL-6XN material relative to conventional austenitic stainless steel (e.g., 304316317, etc.) have a higher tensile strength, while maintaining the excellent material toughness and impact strength, ASME standards specified in the allowable stress values, AL-6XN 40% higher than 316 l, compared to nearly double higher than that of copper - nickel alloy.Physical and mechanical properties of super Austenitic stainless steel (N08367,1.4501) : 1. Density of al-6XN (N08367,1.4501) stainless steel: 8.24g/cm3.2. Tensile strength of al-6XN (N08367,1.4501) stainless steel: B ≥744Mpa.3. Yield strength of al-6XN (N08367,1.4501) stainless steel: B ≥365Mpa.4. Elongation of al-6XN (N08367,1.4501) stainless steel: ≥47%.
Chemical Composition(%):
Carbon (C):0.02 or Less
Manganese (Mn):2.00 or Less
Nickel (Ni):23.5 ~ 25.5,
Silicon (Si):1.0 or Less
Phosphorus (P):0.04 or Less
Sulfur (S):0.01 or Less
Chromium (Cr):20.0 ~ 22.0
Copper (Cu) :0.75 or Less
Molybdenum (Mo) 6.0 ~ 7.0
Nitrogen (N):0.18 ~ 0.25
Al-6XN (N08367,1.4501) super Austenitic stainless steel material characteristics: Al-6XN (N08367,1.4501) stainless steel than [TJC STAINLESS]the standard 300 series alloy, chloride ion has a higher resistance to pitting corrosion, crack corrosion and pressure crack corrosion, in stainless steel Cr, Mo, Ni, C has corrosion resistance to different media.Cr is the representative of corrosion resistance in natural and oxidized environment. The increase of Cr, Mo and Ni content increases the corrosion resistance to pitting; Nickel provides austenite structure; nickel and molybdenum increase the corrosion resistance to chlorine ions in pressure crevices and reduce the corrosion resistance to environment.Al-6xn stainless steel with high nickel (24%) and molybdenum (6.3%) has better resistance to pressure crevices.Molybdenum is resistant to chloride ion pitting and nickel further enhances pitting resistance and provides a higher strength than 300 austenitic stainless steels, so it is often used in thinner parts of the equipment.High levels of chromium, molybdenum, and nickel in al-6xN stainless steel also provide corrosion resistance in forming and welding of the stainless steel.
In addition, Al-6XN stainless steel also has the following characteristics: 1. Excellent corrosion resistance to pitting and crevices under the environment of chloride ion medium.2. Excellent resistance to stress corrosion under the medium of sodium chloride solution.3. High strength and good toughness.Iv. Al-6xn (N08367,1.4501) Super Austenitic stainless steel main applications: High chromium, molybdenum, nickel and nitrogen make AL-6XN have good resistance to chloride ion pitting and crevices corrosion, which makes AL-6XN applied in many environments: flue gas desulfurization spray tower;Reverse osmosis [TJC STAINLESS]seawater desalination equipment and pumps;Chemical reaction kettle and pipeline;Heat exchangers using seawater media;Crude oil splitting distillation column and metal packing;Offshore oil and gas production equipment;Scrubber drums, rollers, grooves, pipes, etc. in pulp bleaching systems.1. Variety classification: It can produce al-6XN seamless pipe, al-6XN steel plate, al-6XN round steel, Al-6XN forgings, al-6XN flange, Al-6Xn ring, al-6XN welded pipe, al-6XN steel strip, al-6XN wire and al-6XN supporting welding materials of various specifications.2. Delivery status: seamless tube: solid solution + acid white, length can be defined;Plate: solid solution, pickling, cutting edge;Welded pipe: solid solution acid white +RT% flaw detection, forgings: anneal + car light;The bar is forged and rolled, its surface polished or polished;The strip is delivered by cold rolling, soft solid solution and deoxidized skin.Silk[TJC STAINLESS] material is delivered in the form of solid solution pickling dish or straight strip, solid solution straight strip and fine polished state.
AL-6XN (N08367) super austenitic stainless steel is a kind of excellent resistance to pitting and crevice corrosion of chlorine ion capacity of super austenitic stainless steel, as a kind of good cost performance of corrosion-resistant alloy, its comprehensive corrosion resistant ability than 316 l had the very big spanning, at the same time [TJC STAINLESS]relative to the C - 276 and other corrosion resistance of nickel base alloy close to its corrosion resistance ability, cost advantage is obvious.Because the visible part of nitrogen is added in the alloy, so that the AL-6XN material relative to conventional austenitic stainless steel (e.g., 304316317, etc.) have a higher tensile strength, while maintaining the excellent material toughness and impact strength, ASME standards specified in the allowable stress values, AL-6XN 40% higher than 316 l, compared to nearly double higher than that of copper - nickel alloy.Physical and mechanical properties of super Austenitic stainless steel (N08367,1.4501) : 1. Density of al-6XN (N08367,1.4501) stainless steel: 8.24g/cm3.2. Tensile strength of al-6XN (N08367,1.4501) stainless steel: B ≥744Mpa.3. Yield strength of al-6XN (N08367,1.4501) stainless steel: B ≥365Mpa.4. Elongation of al-6XN (N08367,1.4501) stainless steel: ≥47%.
Chemical Composition(%):
Carbon (C):0.02 or Less
Manganese (Mn):2.00 or Less
Nickel (Ni):23.5 ~ 25.5,
Silicon (Si):1.0 or Less
Phosphorus (P):0.04 or Less
Sulfur (S):0.01 or Less
Chromium (Cr):20.0 ~ 22.0
Copper (Cu) :0.75 or Less
Molybdenum (Mo) 6.0 ~ 7.0
Nitrogen (N):0.18 ~ 0.25
Al-6XN (N08367,1.4501) super Austenitic stainless steel material characteristics: Al-6XN (N08367,1.4501) stainless steel than [TJC STAINLESS]the standard 300 series alloy, chloride ion has a higher resistance to pitting corrosion, crack corrosion and pressure crack corrosion, in stainless steel Cr, Mo, Ni, C has corrosion resistance to different media.Cr is the representative of corrosion resistance in natural and oxidized environment. The increase of Cr, Mo and Ni content increases the corrosion resistance to pitting; Nickel provides austenite structure; nickel and molybdenum increase the corrosion resistance to chlorine ions in pressure crevices and reduce the corrosion resistance to environment.Al-6xn stainless steel with high nickel (24%) and molybdenum (6.3%) has better resistance to pressure crevices.Molybdenum is resistant to chloride ion pitting and nickel further enhances pitting resistance and provides a higher strength than 300 austenitic stainless steels, so it is often used in thinner parts of the equipment.High levels of chromium, molybdenum, and nickel in al-6xN stainless steel also provide corrosion resistance in forming and welding of the stainless steel.
In addition, Al-6XN stainless steel also has the following characteristics: 1. Excellent corrosion resistance to pitting and crevices under the environment of chloride ion medium.2. Excellent resistance to stress corrosion under the medium of sodium chloride solution.3. High strength and good toughness.Iv. Al-6xn (N08367,1.4501) Super Austenitic stainless steel main applications: High chromium, molybdenum, nickel and nitrogen make AL-6XN have good resistance to chloride ion pitting and crevices corrosion, which makes AL-6XN applied in many environments: flue gas desulfurization spray tower;Reverse osmosis [TJC STAINLESS]seawater desalination equipment and pumps;Chemical reaction kettle and pipeline;Heat exchangers using seawater media;Crude oil splitting distillation column and metal packing;Offshore oil and gas production equipment;Scrubber drums, rollers, grooves, pipes, etc. in pulp bleaching systems.1. Variety classification: It can produce al-6XN seamless pipe, al-6XN steel plate, al-6XN round steel, Al-6XN forgings, al-6XN flange, Al-6Xn ring, al-6XN welded pipe, al-6XN steel strip, al-6XN wire and al-6XN supporting welding materials of various specifications.2. Delivery status: seamless tube: solid solution + acid white, length can be defined;Plate: solid solution, pickling, cutting edge;Welded pipe: solid solution acid white +RT% flaw detection, forgings: anneal + car light;The bar is forged and rolled, its surface polished or polished;The strip is delivered by cold rolling, soft solid solution and deoxidized skin.Silk[TJC STAINLESS] material is delivered in the form of solid solution pickling dish or straight strip, solid solution straight strip and fine polished state.