Product Introduction
UNS N06635 is a nickel-based superalloy with a unique combination of properties. It has excellent thermal stability, low thermal expansion and excellent oxidation resistance to 2000 °F (1093 °C). In addition, the alloy has good high [TJC STAINLESS]temperature and thermal fatigue strength, Hastelloy S wire is a thin nickel alloy circular material, made by cold-drawn wire. Compared with ordinary stainless steel wire, it has better corrosion resistance and high temperature resistance.
Chemical Composition (%):
Alloy-S
C: 0.02 Max;
Cr: 14.5-17;
Ni:Rest;
Fe:3Max;
Mo: 14-16.5;
W:1Max;
Al: 0.1-0.5;[TJC STAINLESS]
La: 0.01-0.1;
Co:2Max;
Si: 0.2-0.75;
Mn: 0.3 1;
P: 0.02 Max.
S: 0.015 Max;
Physical Property
Density: 8.75 g/cm3;
Melting Point:1335-1380℃;
Electrical Resistivity:1.28;
Dilatation Coefficient:11.5*10E-6;
Heat Conductivity:14;
Thermal Diffusivity:3.6*10E-6;[TJC STAINLESS]
Specific Heat Capacity:398;
High Temperature Mechanical Properties
Test Sample Thickness:1.1-1.6MM;
Test Temperature:1093℃;
Tensile Strength Rm:110MPa min;
Yield Strength Rp:52MPa min;
Elongation A5%:46 min;[TJC STAINLESS]
Product Characteristics
1. Excellent thermal stability, low thermal expansion and excellent oxidation resistance;
2. Good high temperature[TJC STAINLESS] and thermal fatigue strength;
3. Maintain its strength and ductility after aging at a temperature of 427 to 871 ° C;
Application Field
Seals for industrial furnaces and gas[TJC STAINLESS] turbine engines
UNS N06635 is a nickel-based superalloy with a unique combination of properties. It has excellent thermal stability, low thermal expansion and excellent oxidation resistance to 2000 °F (1093 °C). In addition, the alloy has good high [TJC STAINLESS]temperature and thermal fatigue strength, Hastelloy S wire is a thin nickel alloy circular material, made by cold-drawn wire. Compared with ordinary stainless steel wire, it has better corrosion resistance and high temperature resistance.
Chemical Composition (%):
Alloy-S
C: 0.02 Max;
Cr: 14.5-17;
Ni:Rest;
Fe:3Max;
Mo: 14-16.5;
W:1Max;
Al: 0.1-0.5;[TJC STAINLESS]
La: 0.01-0.1;
Co:2Max;
Si: 0.2-0.75;
Mn: 0.3 1;
P: 0.02 Max.
S: 0.015 Max;
Physical Property
Density: 8.75 g/cm3;
Melting Point:1335-1380℃;
Electrical Resistivity:1.28;
Dilatation Coefficient:11.5*10E-6;
Heat Conductivity:14;
Thermal Diffusivity:3.6*10E-6;[TJC STAINLESS]
Specific Heat Capacity:398;
High Temperature Mechanical Properties
Test Sample Thickness:1.1-1.6MM;
Test Temperature:1093℃;
Tensile Strength Rm:110MPa min;
Yield Strength Rp:52MPa min;
Elongation A5%:46 min;[TJC STAINLESS]
Product Characteristics
1. Excellent thermal stability, low thermal expansion and excellent oxidation resistance;
2. Good high temperature[TJC STAINLESS] and thermal fatigue strength;
3. Maintain its strength and ductility after aging at a temperature of 427 to 871 ° C;
Application Field
Seals for industrial furnaces and gas[TJC STAINLESS] turbine engines