Product Introduction
UNS N06455 Nickel-based superalloy is a universal corrosion resistant hasselloy, corresponding to the grade NiMo16Cr16Ti, and C4 nitric acid resistant steel is completely different, remember not to be confused, UNS N06455 due to the [TJC STAINLESS]high content of alloying elements, has high temperature resistance, strong corrosion resistance characteristics, but the alloy is prone to crack and porosity. Due to the high strength of the material and the difficulty in forming, the deformation in the welding process is large and difficult to control.
Chemical Composition (%):
N06455 Alloy
Ni:Rest;
Cr: 14.5-17.5;
Fe: 0.3 Max;
Mo:14-17;
Co:2Max;[TJC STAINLESS]
C: 0.009 Max;
Mn:1Max;
Si: 0.05 Max;
S: 0.02 Max;
P: 0.02 Max.
Ti: 0.7 Max;
Physical Property
Density: 8.9 g/cm3;
Melting Point:1325-1370℃;
Tensile Strength Rm:650MPa min;
Yield Strength Rp:280MPa min;
Elongation A5%:40 min;[TJC STAINLESS]
Similar Grades/ Material Names:
GB/T- NS335; UNS- N06455; W.N.R. Alloy C-4
Product Characteristics
1. Excellent thermal stability and toughness;
2. Stress corrosion cracks and oxidizing atmosphere at high temperature have good resistance;
3. Suitable for all kinds[TJC STAINLESS] of hot mineral acids, chlorine-containing media, acetic acid, acetic anhydride, seawater and brine solutions and other corrosive substances;
Application Field
Wet chlorine, hypochlorous acid, [TJC STAINLESS]hydrochloric acid, chloride device
UNS N06455 Nickel-based superalloy is a universal corrosion resistant hasselloy, corresponding to the grade NiMo16Cr16Ti, and C4 nitric acid resistant steel is completely different, remember not to be confused, UNS N06455 due to the [TJC STAINLESS]high content of alloying elements, has high temperature resistance, strong corrosion resistance characteristics, but the alloy is prone to crack and porosity. Due to the high strength of the material and the difficulty in forming, the deformation in the welding process is large and difficult to control.
Chemical Composition (%):
N06455 Alloy
Ni:Rest;
Cr: 14.5-17.5;
Fe: 0.3 Max;
Mo:14-17;
Co:2Max;[TJC STAINLESS]
C: 0.009 Max;
Mn:1Max;
Si: 0.05 Max;
S: 0.02 Max;
P: 0.02 Max.
Ti: 0.7 Max;
Physical Property
Density: 8.9 g/cm3;
Melting Point:1325-1370℃;
Tensile Strength Rm:650MPa min;
Yield Strength Rp:280MPa min;
Elongation A5%:40 min;[TJC STAINLESS]
Similar Grades/ Material Names:
GB/T- NS335; UNS- N06455; W.N.R. Alloy C-4
Product Characteristics
1. Excellent thermal stability and toughness;
2. Stress corrosion cracks and oxidizing atmosphere at high temperature have good resistance;
3. Suitable for all kinds[TJC STAINLESS] of hot mineral acids, chlorine-containing media, acetic acid, acetic anhydride, seawater and brine solutions and other corrosive substances;
Application Field
Wet chlorine, hypochlorous acid, [TJC STAINLESS]hydrochloric acid, chloride device