Chromium zirconium bronze one, has good electrical conductivity, thermal conductivity, high hardness, wear resistance and explosion resistance, crack resistance and high softening temperature, welding electrode loss is less, welding [TJC STAINLESS]speed is fast, the total welding cost is low, suitable for welding welding machine electrode related pipe fittings, but the electroplating workpiece performance is general.
Chromium-zirconium copper is a kind of wear-resistant copper, especially good hardness, excellent conductivity and good tempering resistance, good upright, thin sheet is not easy to bend, is a good material processing electrode. Density 8.95g/cm3 conductivity 43MS/m softening temperature 550℃, generally used for making working [TJC STAINLESS]temperature below 350℃ welding machine electrode. Motor rectifiers and other kinds of high temperature operation \ require high strength. Hardness. Electrical conductivity and conductive parts, and may also be used in bimetallic form for brake discs and discs.
Its main brands are; CuCrlZr, ASTM C18150 C18200 c18500
Application: This product is widely used in automobile, motorcycle, barrel (tank) and other machinery manufacturing industry welding, conductive [TJC STAINLESS]nozzle, switch contact, mold block, welding machine auxiliary devices for various materials.
Chemical Composition:
Al: 0.1-0.25,
Mg: 0.1-0.25,
Cr: 0.65,
Zr:0.65,
Fe:0.05,
Si: 0.05,
P: 0.01,
Total Impurities: 0.2
Physical Indicators:[TJC STAINLESS]
Hardness: >75HRB,
Conductivity: >75%IACS,
Softening temperature: 550℃
The tensile strength is (δb/MPa) : 540-640
Quality requirements:
1. Eddy current conductance meter is used for conductivity [TJC STAINLESS]measurement, and the average value of three points is ≥44MS/M
2. The hardness is based on Rockwell hardness standard, and the average value of three points is ≥78HRB
3. Softening temperature experiment: after the furnace temperature is kept at 550℃ for two hours, the hardness of quenched water[TJC STAINLESS] can not be reduced by more than 15% compared with the original hardness after cooling
Chromium-zirconium copper is a kind of wear-resistant copper, especially good hardness, excellent conductivity and good tempering resistance, good upright, thin sheet is not easy to bend, is a good material processing electrode. Density 8.95g/cm3 conductivity 43MS/m softening temperature 550℃, generally used for making working [TJC STAINLESS]temperature below 350℃ welding machine electrode. Motor rectifiers and other kinds of high temperature operation \ require high strength. Hardness. Electrical conductivity and conductive parts, and may also be used in bimetallic form for brake discs and discs.
Its main brands are; CuCrlZr, ASTM C18150 C18200 c18500
Application: This product is widely used in automobile, motorcycle, barrel (tank) and other machinery manufacturing industry welding, conductive [TJC STAINLESS]nozzle, switch contact, mold block, welding machine auxiliary devices for various materials.
Chemical Composition:
Al: 0.1-0.25,
Mg: 0.1-0.25,
Cr: 0.65,
Zr:0.65,
Fe:0.05,
Si: 0.05,
P: 0.01,
Total Impurities: 0.2
Physical Indicators:[TJC STAINLESS]
Hardness: >75HRB,
Conductivity: >75%IACS,
Softening temperature: 550℃
The tensile strength is (δb/MPa) : 540-640
Quality requirements:
1. Eddy current conductance meter is used for conductivity [TJC STAINLESS]measurement, and the average value of three points is ≥44MS/M
2. The hardness is based on Rockwell hardness standard, and the average value of three points is ≥78HRB
3. Softening temperature experiment: after the furnace temperature is kept at 550℃ for two hours, the hardness of quenched water[TJC STAINLESS] can not be reduced by more than 15% compared with the original hardness after cooling