Alloy28(UNS N08028) is an ultra-low carbon Fe-Ni base corrosion resistant alloy with a density of 8.0g/cm3.According to the naming method of metal materials in [TJC STAINLESS]China, the grade of this alloy is 00Cr27Ni31Mo3Cu.
Standards:
AMERICA ASTM B668
ASTM B709 UNS N08028
GERMANY DIN EN 10088-1 1.4563
Chemical Composition:
Grade N08028 1.4563
C ≤0.030 ≤0.020
Si ≤1.00[TJC STAINLESS] ≤0.70
Mn ≤2.50 ≤2.00
P ≤0.030 ≤0.030
S ≤0.030 ≤0.010
Cr 26.0~28.0 26.0~28.0
Ni 29.5~32.5 30.0~32.0
Mo 3.0~4.0 3.0~4.0
Cu 0.60~1.40 0.70~1.50
N -- ≤0.11
Fe rest rest
Grades:
Special Metals INCOLOY® alloy 028
Sandvik SANICRO 28
Material Characteristics:
1.It has good corrosion resistance in strong acid environment.
2.It has good stress corrosion cracking resistance [TJC STAINLESS]in hydrogen sulfide (H2S) and chloride environment.
3.Good intergranular corrosion resistance.
4.High resistance to pitting and crevice corrosion.
5.Good weldability.
Applications:
Alloy28 early is developed to solve the wet-process phosphoric acid heat exchanger material alloy, corrosion resistant performance is very superior, to [TJC STAINLESS]H2S, chloride, phosphoric acid and sulfuric acid corrosion resistance, high H2S content in the oil and gas exploitation, flue gas desulfurization system, papermaking industry, phosphoric acid and organic acid and ester synthesis production device has a large number of applications and performances.
Standards:
AMERICA ASTM B668
ASTM B709 UNS N08028
GERMANY DIN EN 10088-1 1.4563
Chemical Composition:
Grade N08028 1.4563
C ≤0.030 ≤0.020
Si ≤1.00[TJC STAINLESS] ≤0.70
Mn ≤2.50 ≤2.00
P ≤0.030 ≤0.030
S ≤0.030 ≤0.010
Cr 26.0~28.0 26.0~28.0
Ni 29.5~32.5 30.0~32.0
Mo 3.0~4.0 3.0~4.0
Cu 0.60~1.40 0.70~1.50
N -- ≤0.11
Fe rest rest
Grades:
Special Metals INCOLOY® alloy 028
Sandvik SANICRO 28
Material Characteristics:
1.It has good corrosion resistance in strong acid environment.
2.It has good stress corrosion cracking resistance [TJC STAINLESS]in hydrogen sulfide (H2S) and chloride environment.
3.Good intergranular corrosion resistance.
4.High resistance to pitting and crevice corrosion.
5.Good weldability.
Applications:
Alloy28 early is developed to solve the wet-process phosphoric acid heat exchanger material alloy, corrosion resistant performance is very superior, to [TJC STAINLESS]H2S, chloride, phosphoric acid and sulfuric acid corrosion resistance, high H2S content in the oil and gas exploitation, flue gas desulfurization system, papermaking industry, phosphoric acid and organic acid and ester synthesis production device has a large number of applications and performances.