1.Chemical Composition
A213 TP310HCBN stainless steel seamless pipe uses high-quality raw materials, its chemical composition is mainly iron, chromium, nickel, carbon, manganese and other elements. Among them, the content of chromium is between 19.00%-21.00%, and the content of nickel is between 8.00%-10.00%. This specific chemical composition ratio ensures high corrosion resistance and mechanical properties of the material.
2.Mechanical Properties
A213 TP310HCBN stainless steel seamless pipe has excellent mechanical properties. Its tensile strength usually exceeds 550MPa and its yield strength exceeds 270MPa. In addition, the elongation of the material is high, generally above 35%, which makes the material not easy to break when subjected to complex stresses.
3. Heat Treatment State
After a specific heat treatment process, the internal structure of the A213 TP310HCBN stainless steel seamless pipe is optimized and its mechanical properties are further enhanced. The material after heat treatment has good heat resistance and corrosion resistance, and is suitable for various high temperature and corrosive environments.
4.Low Temperature Impact Test
A213 TP310HCBN stainless steel seamless pipe can maintain good impact toughness in low temperature environment. After low temperature impact test, the material can still maintain high fracture resistance in extremely cold environment, and is suitable for various low temperature application scenarios.
5. Main Application Scenarios
A213 TP310HCBN stainless steel seamless pipe is widely used in petroleum, chemical, electric power and other fields. Due to its excellent corrosion resistance and high mechanical properties, it is often used in the manufacture of pressure vessels, heat exchangers, pipelines and other key equipment. In addition, the material is also suitable for the manufacture of mechanical equipment that needs to withstand high pressures and temperatures.
6.TJC Related Supply Cases
In recent years, TJC has successfully supplied A213 TP310HCBN seamless stainless steel tubing for several large engineering projects. For example, a petrochemical project used TJC's A213 TP310HCBN seamless tubing to manufacture critical pressure vessels and heat exchangers. These devices have shown good performance and stability in the project, meeting the high standards of the customer. With its high-quality products and professional services, TJC has won the trust and praise of customers.
A213 TP310HCBN stainless steel seamless pipe uses high-quality raw materials, its chemical composition is mainly iron, chromium, nickel, carbon, manganese and other elements. Among them, the content of chromium is between 19.00%-21.00%, and the content of nickel is between 8.00%-10.00%. This specific chemical composition ratio ensures high corrosion resistance and mechanical properties of the material.
2.Mechanical Properties
A213 TP310HCBN stainless steel seamless pipe has excellent mechanical properties. Its tensile strength usually exceeds 550MPa and its yield strength exceeds 270MPa. In addition, the elongation of the material is high, generally above 35%, which makes the material not easy to break when subjected to complex stresses.
3. Heat Treatment State
After a specific heat treatment process, the internal structure of the A213 TP310HCBN stainless steel seamless pipe is optimized and its mechanical properties are further enhanced. The material after heat treatment has good heat resistance and corrosion resistance, and is suitable for various high temperature and corrosive environments.
4.Low Temperature Impact Test
A213 TP310HCBN stainless steel seamless pipe can maintain good impact toughness in low temperature environment. After low temperature impact test, the material can still maintain high fracture resistance in extremely cold environment, and is suitable for various low temperature application scenarios.
5. Main Application Scenarios
A213 TP310HCBN stainless steel seamless pipe is widely used in petroleum, chemical, electric power and other fields. Due to its excellent corrosion resistance and high mechanical properties, it is often used in the manufacture of pressure vessels, heat exchangers, pipelines and other key equipment. In addition, the material is also suitable for the manufacture of mechanical equipment that needs to withstand high pressures and temperatures.
6.TJC Related Supply Cases
In recent years, TJC has successfully supplied A213 TP310HCBN seamless stainless steel tubing for several large engineering projects. For example, a petrochemical project used TJC's A213 TP310HCBN seamless tubing to manufacture critical pressure vessels and heat exchangers. These devices have shown good performance and stability in the project, meeting the high standards of the customer. With its high-quality products and professional services, TJC has won the trust and praise of customers.