0Cr15Ni5Cu2Ti martensitic precipitated hardened stainless steels with copper as the main strengthening element.Martensite precipitates hardened stainless steels with copper as the main hardening element, most commonly at [TJC STAINLESS]17-4pH.0Cr15Ni5Cu2Ti can be seen on the basis of 17-4PH composition of reducing chromium and copper, nickel, and titanium instead of niobium steel, and 15-5PH is very similar.
Component Specification
STANDARD Y.J0060(A) Y.J0061(A)
variety Bar Plate
C ≤0.08 ≤0.08
Si ≤0.70 ≤0.70
Mn ≤1.00 ≤1.00
P ≤0.020 ≤0.020
S ≤0.018 ≤0.018
Cr 13.5~14.8 14.0~15.0
Ni 4.8~5.8 4.7~5.7
Cu 1.75~2.50 1.75~2.50
Ti 0.03~0.15[TJC STAINLESS] 0.15~0.30
The performance characteristics of:
0Cr15Ni5Cu2Ti steel has the following characteristics:
(1)High strength is obtained after aging hardening.
(2)The corrosion resistance is equal to 17-4PH.
(3)Good welding performance.
(4)Weak cold forming ability.
(5)Good thermal forming performance.
(6)Good cutting performance in both [TJC STAINLESS]solid solution and aging state.
Applications:
0Cr15Ni5Cu2Ti steel has good strength and toughness, good oxidation resistance at medium temperature, and good chemical stability in corrosive medium. It is usually used in the manufacture of important load-bearing [TJC STAINLESS]components such as aero-engine combustion chamber casing and tapered beam installation edge.
Component Specification
STANDARD Y.J0060(A) Y.J0061(A)
variety Bar Plate
C ≤0.08 ≤0.08
Si ≤0.70 ≤0.70
Mn ≤1.00 ≤1.00
P ≤0.020 ≤0.020
S ≤0.018 ≤0.018
Cr 13.5~14.8 14.0~15.0
Ni 4.8~5.8 4.7~5.7
Cu 1.75~2.50 1.75~2.50
Ti 0.03~0.15[TJC STAINLESS] 0.15~0.30
The performance characteristics of:
0Cr15Ni5Cu2Ti steel has the following characteristics:
(1)High strength is obtained after aging hardening.
(2)The corrosion resistance is equal to 17-4PH.
(3)Good welding performance.
(4)Weak cold forming ability.
(5)Good thermal forming performance.
(6)Good cutting performance in both [TJC STAINLESS]solid solution and aging state.
Applications:
0Cr15Ni5Cu2Ti steel has good strength and toughness, good oxidation resistance at medium temperature, and good chemical stability in corrosive medium. It is usually used in the manufacture of important load-bearing [TJC STAINLESS]components such as aero-engine combustion chamber casing and tapered beam installation edge.